Thesis  

perbedaanPERBEDAAN MECHANICAL PROPERTIES CAMPURAN NANOPARTIKEL SEMEN PORTLAND PUTIH INDONESIA-ZrO2-UDMA DENGAN DAN TANPA PENAMBAHAN NANOSILIKA SEBAGAI BAHAN PULP CAPPING

---

• Ketersediaan
• Informasi Detil
• Deskripsi
• Versi lain/terkait
• Komentar

• Code	CallNo	Lokasi	Ketersediaan
  TH 1000	617.63 Ary P	Sekeloa (Konservasi Gigi)	Tersedia namun tidak untuk dipinjamkan - No Loan

• Perpustakaan	Fakultas Kedokteran Gigi
  Judul Seri	-
  No. Panggil	617.63 Ary P
  Penerbit	PPDGS Konseravasi Gigi Unpad : FKG Sekeloa Unpad., 2023
  Deskripsi Fisik	xiv, 84 hlm, ilus; 21x30 cm
  Bahasa	Indonesia
  ISBN/ISSN	160621200005
  Klasifikasi	617.63
  Tipe Isi	-
  Tipe Media	-
  Tipe Pembawa	-
  Edisi	-
  Subyek	compressive strength nanosilika pulp capping Semen portland putih Indonesia , Flexural strength , Modulus of elasticity
  Info Detil Spesifik	-
  Pernyataan Tanggungjawab	Shyntia Dewi Aryani (Author)

• ABSTRAK Tindakan perawatan pulpa vital seperti pulp capping dapat menjadi pilihan dalam mempertahankan vitalitas pulpa dengan cara mencegah infiltrasi bakteri dan merangsang pembentukan dentin tersier. Syarat bahan pulp capping harus memiliki sifat mekanis yang baik dalam menahan tekanan kunyah yang terdistribusi pada gigi dan bahan restorasi di atasnya, beberapa di antaranya seperti compressive strength, flexural strengthnya dan modulus of elasticity. Kandungan semen Portland putih Indonesia (SPPI) memiliki komposisi yang sama dengan bahan MTA dalam penggunaannya sebagai bahan pulp capping. Tujuan dari penelitian ini adalah untuk membuat bahan pulp capping dengan campuran nanopartikel SPPIZrO2-UDMA dengan dan tanpa penambahan nanosilika untuk menganalisis nilai compressive strength, flexural strength, dan modulus of elasticity. Pembuatan sampel campuran nanopartikel SPPI-ZrO2-UDMA dengan dan tanpa penambahan nanosilika dimulai melalui proses sintesis nanopartikel SPPI lalu dicampurkan dengan ZrO2 kemudian dicampurkan dengan UDMA dan nanosilika. Hasil pengujian compressive strength, flexural strength, dan modulus of elasticity dilakukan dengan Universal Testing Machine (UTM) sesuai dengan ISO 9971-1dan ISO 4049. Analisis data menggunakan uji ANAVA dan Post-hoc Independent t-test untuk mengetahui nilai perbedaan keduanya.Hasil penelitian menunjukkan nilai rata-rata compressive strength tertinggi campuran nanopartikel SPPI-ZrO2-UDMA dengan nanosilika yaitu 115.52 MPa dan SPPI-ZrO2-UDMA tanpa nanosilika 105.60 MPa. Nilai rata-rata flexural strength tertinggi campuran nanopartikel SPPIZrO2-UDMA dengan nanosilika yaitu 61.39 MPa dan SPPI-ZrO2-UDMA tanpa nanosilika 83.53 MPa. Nilai rata-rata modulus of elasticity tertinggi campuran nanopartikel SPPI-ZrO2-UDMA dengan nanosilika yaitu 7552.82 MPa dan SPPIZrO2-UDMA tanpa nanosilika 7191.08 MPa. Hasil analisis statistik menunjukkan perbedaan signifikan pada kedua bahan tersebut. Kata Kunci: Pulp capping, Semen Portland Putih Indonesia, Nanosilika, Compressive strength, Flexural strength, Modulus of elasticity xiv ABSTRACT Vital pulp therapy such as pulp capping can be an option in maintaining pulp vitality by preventing bacterial infiltration and stimulating tertiary dentin formation. Pulp capping materials must have good mechanical properties to withstand the masticatory forces on the tooth and the restoration material above, such as compressive strength, flexural strength and modulus of elasticity. Indonesian white Portland cement (SPPI) has the same composition with MTA material use as a pulp capping material. The purpose of this research is to make pulp capping materials with a mixture of SPPI-ZrO2-UDMA nanoparticles with and without the addition of nanosilica to analyze the compressive strength, flexural strength, and modulus of elasticity values. The preparation of SPPI-ZrO2-UDMA nanoparticle mixture samples with and without the addition of nanosilica begins through the process of synthesizing SPPI nanoparticles then mixed with ZrO2, mixed with UDMA and nanosilica. Compressive strength, flexural strength, and modulus of elasticity testing were carried out using Universal Testing Machine (UTM) in accordance with ISO 9971-1 and ISO 4049. Data analysis used ANOVA test and Post-hoc Independent t-test to determine the value of the difference between the two. The results showed that the highest mean compressive strength value of SPPI-ZrO2-UDMA nanoparticle with the addition of nanosilica was 115.52 MPa and SPPI-ZrO2-UDMA without nanosilica was 105.60 MPa. The highest mean flexural strength value of SPPI-ZrO2-UDMA nanoparticle with the addition of nanosilica is 61.39 MPa and SPPI-ZrO2-UDMA without nanosilica is 83.53 MPa. The highest mean value of modulus of elasticity of SPPI-ZrO2-UDMA nanoparticle with the addition of nanosilica is 7552.82 MPa and SPPI-ZrO2- UDMA without nanosilica is 7191.08 MPa. The results of statistical analysis showed significant differences in the two materials. Key words: Pulp capping, Indonesian White Portland Cement, Nanosilica, Compressive strength, Flexural strength, Modulus of elasticity